Marei, Ahmed K. and Saleh, Ayed N. (2026) Effect of bulk Defect Concentration on Capacitance Characteristics of an Experimentally Calibrated CIGS Solar Cell Using SCAPS-1D via Admittance Spectroscopy. Central Asian Journal of Medical and Natural Science, 7 (4). ISSN 2660-4159

Text CAJMNS_3342_Effect+of+bulk+Defect+Concentration.pdf Download (914kB)

Abstract

In this work, the combined effect of temperature (184–304 K) and defect concentration (1.4 × 10¹²–1.4 × 10¹⁶ cm⁻³) on the capacitance characteristics of a calibrated Cu(In,Ga)Se₂ (CIGS) solar cell was systematically investigated using Solar Cell Capacitance Simulator in one dimension (SCAPS-1D) via admittance spectroscopy. The results show that the characteristic frequency shifts significantly with temperature from approximately (~3.7×102 Hz) at (184 K) to (~5.1× 106 Hz) at (304 K), indicating a thermally activated emission process spanning nearly three orders of magnitude. Meanwhile, increasing defect concentration reduces the low-frequency capacitance from (~65.7 nF/cm²) to (~61.4 nF/cm²) and enhances the visibility of the defect response without altering its intrinsic energy level. The derivative analysis (−ƒ×dC/dƒ) enabled precise extraction of the characteristic frequencies, especially at high defect concentration (1.4 × 10¹⁶ cm⁻³), where sharp and well-defined peaks were observed. The Arrhenius analysis yielded an activation energy of (0.328 eV), which is lower than the introduced defect level (0.88 eV), reflecting the effective emission barrier relative to the conduction band. These findings confirm that temperature controls the dynamic defect response, while defect concentration primarily governs the amplitude and detectability, providing a reliable framework for defect characterization and optimization of CIGS solar cells.

Item Type:	Article
Uncontrolled Keywords:	CIGS Solar Cells, SCAPS-1D, Admittance Spectroscopy, Bulk Defects, Activation Energy
Subjects:	H Social Sciences
Depositing User:	admin eprints
Date Deposited:	18 Jul 2026 15:14
Last Modified:	18 Jul 2026 15:14
URI:	http://eprints.umsida.ac.id/id/eprint/16788

Actions (login required)

View Item